Corrosion resistance
Contains high chromium (22%-24%) and nickel (12%-15%) elements, forming a dense oxide film, which can protect the steel surface in high temperature and corrosive environments, and has better corrosion resistance than SUS304 stainless steel.
Heat resistance
Can withstand repeated heating below 980℃, and still maintain strength and toughness at high temperatures, suitable for 800-1000℃ working environments.
Processing performance
Adding sulfur elements, the friction during cutting is small, the surface finish is high, and it is suitable for precision processing.
Applicable scenarios
Widely used in high temperature and high pressure scenarios such as boilers, industrial furnaces, and chemical equipment, and also suitable for precision machining.
| Product Name | Stainless Steel Ber |
| Padrão | ASTM,JIS,DIN,GB,AISI,DIN,EN |
| Material | 201, 202, 301, 301L, 304, 304L, 316, 316L, 321, 310S, 904L, 410, 420J2, 430, 2205, 2507, 321H, 347, 347H, 403, 405, 409, 420, 430, 631, 904L, 305, 301L, 317, 317L, 309, 309S 310 |
| Técnica | Estirados a frio, laminados a quente, laminados a frio e outros. |
| Diameter | 6-12 mm ou personalizável |
| Comprimento | 1000 – 6000mm or Customizable |
| Tratamento de superfície | BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D |
| Origem | China |
| Código SH | 7220204000 |
| Prazo de entrega | {Tempo de entrega} |
| Serviço pós-venda | 24 horas em linha |
| Capacidade de produção | {Capacidade de produção} |
| Condições de preço | EXW, FOB, CIF, CRF, CNF or others |
| Porta de carregamento | {Port} |
| Prazo de pagamento | TT, LC, Cash, Paypal, DP, DA, Western Union or Others. |
| Aplicação | 1. Louça de mesa, armários, condutas interiores, aquecedores de água, caldeiras, banheiras |
| 2. Peças para automóveis | |
| 3. equipamentos médicos, materiais de construção, produtos químicos, indústria alimentar, agricultura, componentes de navios, etc. | |
| Embalagem | Pacote, saco de PVC, cinto de nylon, braçadeira de cabo, pacote padrão de exportação em condições de navegar ou como pedido. |
| Serviço de processamento | Dobragem, Soldadura, Desbobinagem, Puncionamento, Corte e outros. |
| Tolerância | ±1% |
| MOQ | {MOQ} |
Composição do aço inoxidável
O aço é uma liga de ferro e carbono. Os aços inoxidáveis são aços que contêm pelo menos 10,5% de crómio, menos de 1,2% de carbono e outros elementos de liga. A resistência à corrosão do aço inoxidável e
As propriedades mecânicas podem ser melhoradas pela adição de outros elementos, como o níquel, o molibdénio, o titânio, o nióbio, o manganês, etc.
| Grau | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu |
| 201 | ≤0.15 | ≤0.75 | 5.5~7.5 | ≤0.060 | ≤0.03 | 16.00~18.00 | 3.5~5.5 | – | – | 0.08 |
| 202 | ≤0.15 | ≤1.00 | 7.5~10.00 | ≤0.060 | ≤0.03 | 17.00~19.00 | 4.0~6.0 | – | ≤0.25 | |
| 301 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 6.00~8.00 | – | ||
| 302 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 17.00~19.00 | 8.00~10.00 | – | ||
| 304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 8.00~10.50 | – | ||
| 304L | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 9.00~13.00 | – | ||
| 310S | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 24.00~26.00 | 19.00~22.00 | – | ||
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 10.00~14.00 | 2.00~3.00 | ||
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 12.00~15.00 | 2.00~3.00 | ||
| 321 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 17.00~19.00 | 9.00~13.00 | – | ||
| 430 | ≤0.12 | ≤0.75 | ≤1.00 | ≤0.040 | ≤0.03 | 16.00~18.00 | – | |||
| 2205 | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.030 | ≤0.015 | 22.00~23.00 | 4.5~6.5 | 2.5~3.5 | ||
| 2507 | ≤0.03 | ≤0.08 | ≤1.20 | ≤0.035 | ≤0.015 | 24.00~26.00 | 6.00~8.00 | 3.0~5.0 | ||
| 904L | ≤0.02 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.035 | 19.00~23.00 | 23.00~28.00 | 4.0~5.0 | 1.0~2.0 | |
| INCONEL028 | ≤0.03 | ≤1.00 | ≤2.50 | ≤0.030 | ≤0.030 | ≤28.0 | ≤34.0 | ≤4.0 | ≤1.4 | |
| MONEL400 | ≤0.30 | ≤0.5 | ≤2.00 | – | ≤0.024 | – | ≥63.0 | – | ≤34.0 | |
| INCONEL800 | ≤0.10 | ≤1.00 | ≤1.50 | – | ≤0.015 | ≤23.0 | ≤35 | 4.0~5.0 | – | ≤0.75 |