The characteristics of SS410 stainless steel coil are as follows:
High strength: After heat treatment, the yield strength of SUS410 stainless steel bar is ≥345MPa, and the tensile strength is ≥540MPa.
Good corrosion resistance: SUS410 stainless steel can resist corrosion from some strong acids, strong alkalis and seawater.
Good machining performance: SUS410 stainless steel has good weldability, abrasion resistance, bending processability, etc.
Good high temperature oxidation resistance: SUS410 stainless steel can maintain stable performance in high temperature environment (such as below 800℃), and can form a dense passivation film in high temperature atmosphere, thus having good oxidation resistance
| Product Name | Stainless Steel Coil/Strip |
| Standard | ASTM,JIS,DIN,GB,AISI,DIN,EN |
| Material | 201, 202, 301, 301L, 304, 304L, 316, 316L, 321, 310S, 904L, 410, 420J2, 430, 2205, 2507, 321H, 347, 347H, 403, 405, 409, 420, 430, 631, 904L, 305, 301L, 317, 317L, 309, 309S 310 |
| Technique | Cold drawn, Hot rolled, Cold rolled and Others. |
| Width | 6-12mm or Customizable |
| Thickness | 1-12mm or Customizable |
| Length | 1000 – 6000mm or Customizable |
| Surface Treatment | BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D |
| Origin | China |
| HS Code | 7219131200 |
| Delivery Time | {Delivery Time} |
| After-sales Service | 24 hours online |
| Production Capacity | {Production Capacity} |
| Price Terms | EXW, FOB, CIF, CRF, CNF or Others. |
| Loading Port | {Port} |
| Payment Term | TT, LC,Cash, Paypal, DP, DA,Western Union or Others. |
| Application | 1. Tableware, cabinets, indoor pipelines, water heaters, boilers, bathtubs |
| 2. Automotive parts | |
| 3.Medicale quipment, building materials, chemicals, food industry, agriculture, ship components, etc. | |
| Packaging | Bundle, PVC Bag, Nylon Belt, Cable Tie, Standard export seaworthy package or as Request. |
| Processing Service | Bending, Welding, Decoiling, Punching, Cutting and Others. |
| Tolerance | ±1% |
| MOQ | {MOQ} |
Composition of Stainless Steel
Steel is an alloy of iron and carbon. Stainless steels are steels containing at least 10.5% chromium, less than 1.2% carbon and other alloying elements. Stainless steel’s corrosion resistance and
mechanical properties can be further enhanced by adding other elements, such as nickel, molybdenum, titanium, niobium, manganese, etc.
| Grade | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu |
| 201 | ≤0.15 | ≤0.75 | 5.5~7.5 | ≤0.060 | ≤0.03 | 16.00~18.00 | 3.5~5.5 | – | – | 0.08 |
| 202 | ≤0.15 | ≤1.00 | 7.5~10.00 | ≤0.060 | ≤0.03 | 17.00~19.00 | 4.0~6.0 | – | ≤0.25 | |
| 301 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 6.00~8.00 | – | ||
| 302 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 17.00~19.00 | 8.00~10.00 | – | ||
| 304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 8.00~10.50 | – | ||
| 304L | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 9.00~13.00 | – | ||
| 310S | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 24.00~26.00 | 19.00~22.00 | – | ||
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 10.00~14.00 | 2.00~3.00 | ||
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 12.00~15.00 | 2.00~3.00 | ||
| 321 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 17.00~19.00 | 9.00~13.00 | – | ||
| 430 | ≤0.12 | ≤0.75 | ≤1.00 | ≤0.040 | ≤0.03 | 16.00~18.00 | – | |||
| 2205 | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.030 | ≤0.015 | 22.00~23.00 | 4.5~6.5 | 2.5~3.5 | ||
| 2507 | ≤0.03 | ≤0.08 | ≤1.20 | ≤0.035 | ≤0.015 | 24.00~26.00 | 6.00~8.00 | 3.0~5.0 | ||
| 904L | ≤0.02 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.035 | 19.00~23.00 | 23.00~28.00 | 4.0~5.0 | 1.0~2.0 | |
| INCONEL028 | ≤0.03 | ≤1.00 | ≤2.50 | ≤0.030 | ≤0.030 | ≤28.0 | ≤34.0 | ≤4.0 | ≤1.4 | |
| MONEL400 | ≤0.30 | ≤0.5 | ≤2.00 | – | ≤0.024 | – | ≥63.0 | – | ≤34.0 | |
| INCONEL800 | ≤0.10 | ≤1.00 | ≤1.50 | – | ≤0.015 | ≤23.0 | ≤35 | 4.0~5.0 | – | ≤0.75 |
Surface Selection