Corrosion resistance
Molybdenum (2%-3%) significantly improves the resistance to pitting and crevice corrosion, especially in chloride environments, seawater and high temperature environments, and is comparable to platinum in corrosion resistance.
Mechanical properties
Tensile strength ≥480MPa, yield strength ≥177MPa, elongation ≥40%, strong work hardening and non-magnetic in solid solution state.
Processing characteristics
The surface gloss of cold-rolled products is high, and the mechanical properties are better after heat treatment (tensile strength can reach 620MPa).
Application scenarios
Widely used in chemical equipment, marine engineering, medical implants and food processing, but avoid contact with hydrofluoric acid or concentrated hot hydrochloric acid.
| Product Name | Stainless Steel Ber |
| Estándar | ASTM,JIS,DIN,GB,AISI,DIN,EN |
| Material | 201, 202, 301, 301L, 304, 304L, 316, 316L, 321, 310S, 904L, 410, 420J2, 430, 2205, 2507, 321H, 347, 347H, 403, 405, 409, 420, 430, 631, 904L, 305, 301L, 317, 317L, 309, 309S 310 |
| Technique | Cold drawn, Hot rolled, Cold rolled and Others. |
| Diameter | 6-12mm or Customizable |
| Longitud | 1000 – 6000mm or Customizable |
| Surface Treatment | BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D |
| Origin | China |
| HS Code | 7220204000 |
| Delivery Time | {Delivery Time} |
| After-sales Service | 24 hours online |
| Production Capacity | {Production Capacity} |
| Price Terms | EXW, FOB, CIF, CRF, CNF or others |
| Loading Port | {Port} |
| Payment Term | TT, LC, Cash, Paypal, DP, DA, Western Union or Others. |
| Application | 1. Tableware, cabinets, indoor pipelines, water heaters, boilers, bathtubs |
| 2. Automotive parts | |
| 3.Medicale quipment, building materials, chemicals, food industry, agriculture, ship components, etc. | |
| Packaging | Bundle, PVC Bag, Nylon Belt, Cable Tie, Standard export seaworthy package or as Request. |
| Processing Service | Bending, Welding, Decoiling, Punching, Cutting and Others. |
| Tolerance | ±1% |
| MOQ | {MOQ} |
Composition of Stainless Steel
Steel is an alloy of iron and carbon. Stainless steels are steels containing at least 10.5% chromium, less than 1.2% carbon and other alloying elements. Stainless steel’s corrosion resistance and
mechanical properties can be further enhanced by adding other elements, such as nickel, molybdenum, titanium, niobium, manganese, etc.
| Grado | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu |
| 201 | ≤0.15 | ≤0.75 | 5.5~7.5 | ≤0.060 | ≤0.03 | 16.00~18.00 | 3.5~5.5 | – | – | 0.08 |
| 202 | ≤0.15 | ≤1.00 | 7.5~10.00 | ≤0.060 | ≤0.03 | 17.00~19.00 | 4.0~6.0 | – | ≤0.25 | |
| 301 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 6.00~8.00 | – | ||
| 302 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 17.00~19.00 | 8.00~10.00 | – | ||
| 304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 8.00~10.50 | – | ||
| 304L | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 9.00~13.00 | – | ||
| 310S | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 24.00~26.00 | 19.00~22.00 | – | ||
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 10.00~14.00 | 2.00~3.00 | ||
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 12.00~15.00 | 2.00~3.00 | ||
| 321 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 17.00~19.00 | 9.00~13.00 | – | ||
| 430 | ≤0.12 | ≤0.75 | ≤1.00 | ≤0.040 | ≤0.03 | 16.00~18.00 | – | |||
| 2205 | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.030 | ≤0.015 | 22.00~23.00 | 4.5~6.5 | 2.5~3.5 | ||
| 2507 | ≤0.03 | ≤0.08 | ≤1.20 | ≤0.035 | ≤0.015 | 24.00~26.00 | 6.00~8.00 | 3.0~5.0 | ||
| 904L | ≤0.02 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.035 | 19.00~23.00 | 23.00~28.00 | 4.0~5.0 | 1.0~2.0 | |
| INCONEL028 | ≤0.03 | ≤1.00 | ≤2.50 | ≤0.030 | ≤0.030 | ≤28.0 | ≤34.0 | ≤4.0 | ≤1.4 | |
| MONEL400 | ≤0.30 | ≤0.5 | ≤2.00 | – | ≤0.024 | – | ≥63.0 | – | ≤34.0 | |
| INCONEL800 | ≤0.10 | ≤1.00 | ≤1.50 | – | ≤0.015 | ≤23.0 | ≤35 | 4.0~5.0 | – | ≤0.75 |