The characteristics of 316l stainless steel wire rod mainly include:
Corrosion resistance: 316l stainless steel wire rod has better corrosion resistance than 304 stainless steel due to the presence of molybdenum (Mo), especially in terms of pitting and chloride corrosion resistance.
High temperature performance: Under high temperature conditions, 316l stainless steel wire rod has good oxidation resistance. It can be used intermittently below 1600 degrees and continuously below 700 degrees.
Welding performance: 316l stainless steel wire rod has good welding performance and can be welded by all standard welding methods. When welding, 316Cb, 316L or 309Cb stainless steel filler rods or welding rods can be used for welding according to the purpose
Mechanical properties: The tensile strength of 316l stainless steel wire rod is not less than 485MPa, the yield strength is not less than 170MPa, the elongation is not less than 30%, and the area reduction is not less than 40%
Density and hardness: The density of 316l stainless steel wire rod is 7.93g/cm³, and the hardness is HRB<90, HV<200, HBS<187
| Name | Stainless steel  wire rods |
| Main material | 201 /202 /204/ 207/ 207Cu /301 /302 /303 /303B /304 /304L /304N /308 /308L /308LSi /309 / |
| Â Â Â Â 309L /309LSi /309S /309Si /310/ 310S /314 /316 /316L /316LSi /321 /330 /347 /348 /389 /410 / | |
| Â Â 420/430 | |
| Surface finish | Matt  or bright |
| Diameter | 0.03-20mm  or custom |
| Standard | GB/AISIIS/SUS/UNS/DIN/BS |
| Länge | 500m-2000m/reel  or as your requirement |
| Anmeldung | Spring, Â BBQ mesh, wire forms, cable, clothes hanger, dish rack, |
| Artistic  work, fishery, steel  wire ball, precise instrument, medical  instrument, oil field etc. | |
| Features | Bright  surface/good  formability/good elasticity/High dimensional  accuracy/anti- |
|   corrosion/acid-resistant/high  temperature resistant/wear-resistant/ hard to  age/high | |
|   tensile strength/chemical  composition stability/purity | |
| Price Term | Ex-Work，FOB,  CIF, CFR |
| Package | 1. Â Carton package |
| 2. Â Wooden package | |
| 3. Â As your requirement |
Zusammensetzung von rostfreiem Stahl
Stahl ist eine Legierung aus Eisen und Kohlenstoff. Nichtrostende Stähle sind Stähle mit mindestens 10,5% Chrom, weniger als 1,2% Kohlenstoff und anderen Legierungselementen. Die Korrosionsbeständigkeit von rostfreiem Stahl und
Die mechanischen Eigenschaften können durch Zugabe anderer Elemente wie Nickel, Molybdän, Titan, Niob, Mangan usw. weiter verbessert werden.
| Klasse | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu |
| 201 | ≤0.15 | ≤0.75 | 5.5~7.5 | ≤0.060 | ≤0.03 | 16.00~18.00 | 3.5~5.5 | – | – | 0.08 |
| 202 | ≤0.15 | ≤1.00 | 7.5~10.00 | ≤0.060 | ≤0.03 | 17.00~19.00 | 4.0~6.0 | – | ≤0.25 | |
| 301 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 6.00~8.00 | – | ||
| 302 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 17.00~19.00 | 8.00~10.00 | – | ||
| 304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 8.00~10.50 | – | ||
| 304L | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 9.00~13.00 | – | ||
| 310S | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 24.00~26.00 | 19.00~22.00 | – | ||
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 10.00~14.00 | 2.00~3.00 | ||
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 12.00~15.00 | 2.00~3.00 | ||
| 321 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 17.00~19.00 | 9.00~13.00 | – | ||
| 430 | ≤0.12 | ≤0.75 | ≤1.00 | ≤0.040 | ≤0.03 | 16.00~18.00 | – | |||
| 2205 | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.030 | ≤0.015 | 22.00~23.00 | 4.5~6.5 | 2.5~3.5 | ||
| 2507 | ≤0.03 | ≤0.08 | ≤1.20 | ≤0.035 | ≤0.015 | 24.00~26.00 | 6.00~8.00 | 3.0~5.0 | ||
| 904L | ≤0.02 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.035 | 19.00~23.00 | 23.00~28.00 | 4.0~5.0 | 1.0~2.0 | |
| INCONEL028 | ≤0.03 | ≤1.00 | ≤2.50 | ≤0.030 | ≤0.030 | ≤28.0 | ≤34.0 | ≤4.0 | ≤1.4 | |
| MONEL400 | ≤0.30 | ≤0.5 | ≤2.00 | – | ≤0.024 | – | ≥63.0 | – | ≤34.0 | |
| INCONEL800 | ≤0.10 | ≤1.00 | ≤1.50 | – | ≤0.015 | ≤23.0 | ≤35 | 4.0~5.0 | – | ≤0.75 |